[1]赵志曼,王思骅,全思臣,等.新型石蜡防水剂对磷建筑石膏性能的影响[J].西安建筑科技大学学报(自然科学版),2019,51(06):791-796.[doi:10.15986/j.1006-7930.2019.06.004]
 ZHAO Zhiman,WANG Sihua,QUAN Sichen,et al.Effect of new wax waterproofing agent on properties of phosphorus building gypsum[J].J. Xi’an Univ. of Arch. & Tech.(Natural Science Edition),2019,51(06):791-796.[doi:10.15986/j.1006-7930.2019.06.004]
点击复制

新型石蜡防水剂对磷建筑石膏性能的影响()
分享到:

西安建筑科技大学学报(自然科学版)[ISSN:1006-7930/CN:61-1295/TU]

卷:
51
期数:
2019年06期
页码:
791-796
栏目:
出版日期:
2019-12-31

文章信息/Info

Title:
Effect of new wax waterproofing agent on properties of phosphorus building gypsum
文章编号:
1006-7930(2019)06-0791-06
作者:
赵志曼2王思骅1全思臣3赵彬宇1张毅1李丹1
(1.昆明理工大学 建筑工程学院,云南 昆明 650500;2.云南省土木工程防灾重点实验室,云南 昆明 650500;3.云南凝创环保科技有限公司,云南 昆明 650500)
Author(s):
ZHAO Zhiman2WANG Sihua1QUAN Sichen2ZHAO Binyu1ZHANG Yi1LI Dan1
(1.Faculty of Architecture and Engineering,Kunming University of Science and Technology,Kunming 650500, China;2.Yunnan Province Civil Engineering Disaster Prevention Key Laboratory,Kunming 650500, China;3.Yunnan Ningchuang Environmental Protection Technology Co., Ltd.,Kunming 650500, China)
关键词:
石蜡表面活性剂磷建筑石膏防水
Keywords:
paraffin surfactant phosphorus building gypsum waterproof
分类号:
TU578.1;TS6536
DOI:
10.15986/j.1006-7930.2019.06.004
文献标志码:
A
摘要:
在石蜡中加入十二烷基苯磺酸钠、吐温80等表面活性剂制备出新型石蜡防水剂,掺入到磷建筑石膏中制备试块,再分别与掺入石蜡和空白组进行对比,分析了其防水机理和对磷建筑石膏性能的影响,以及不同类型、掺量表面活性剂对新型石蜡乳液的作用机理.分析可得,掺入的新型石蜡防水剂所制备的磷建筑石膏试块具有较好的防水性能,且当新型石蜡防水剂掺入量为06%的时,软化系数达到0.78,与空白组相比提高了90%.当掺入量为1%时,磷建筑石膏吸水率与掺入量为0.2%相比降低了41.9%,比空白组降低了60.4%.
Abstract:
A new paraffin waterproofing agent was prepared by adding Sodium dodecylbenzene sulfonate and Twain 0 .80 surfactants into the paraffin wax, and the test blocks were added to phosphorus building gypsum. The waterproofing mechanism and the influence on the energy properties of phosphogypsum gypsum were analyzed respectively, and the mechanism of different types and dosage of surfactants on the new paraffin emulsion was compared. The results show that the phosphorus building gypsum sample prepared by adding new paraffin waterproofing agent has better waterproofing performance, and when the new paraffin waterproofing agent is 0.6%, the softening coefficient reaches 0.78, which is 90% higher than that of the blank group. When the content of phosphorus building gypsum is 1%, the water absorption of phosphorus building gypsum is 41.9% lower than that of 0.2% and 60.4% lower than that of blank group.

参考文献/References:

[1]孙志立. 中国磷石膏资源化利用的展望与思考[J].硫酸工业, 2016(1):55-58.

SUN Zhili. Prospect and thinking on utilization of phosphogypsum resources in China [J]. Sulfuric Acid Jndustry, 2016 (1): 55-58.
[2]李欣霖, 纪利俊, 陈葵, 等. 有机溶剂浸取法净化磷石膏[J]. 化工矿物与加工, 2018(3): 23-27.
LI Xinlin, JI Lijun, CHEN Kui, et al. Purification of phosphogypsum by organic solvent extraction [J]. Chemical Minerals and Processing, 2018(3): 23-27.
[3]ZOLOTUKHIN S N, KUKINA O B, ABRAMENKO A A, et al. Energyefficient unburned technologies for the use of phosphogypsum[J]. IOP Conference Series: Earth and Environmental Science, 2017, 90:012088.
[4]GARG M, MINOCHA A K, JAIN N. Environment hazard mitigation of waste gypsum and chalk: Use in construction materials[J]. Construction and Building Materials, 2011, 25(2):944949.
[5]李美, 彭家惠, 张建新, 等. 磷建筑石膏的特性及其改性[J]. 硅酸盐通报, 2012, 31(3):553-558.
LI Mei, PENG Jiahui, ZHANG Jianxin, et al. Characteristics and modification of phosphogypsum [J]. Silicate Bulletin, 2012, 31 (3):553-558.
[6]RAMSSON E S, CHOLGER D, DIONISE A, et al. Characterization of fastscan cyclic voltammetric electrodes using paraffin as an effective sealant with in vitro and in vivo applications[J]. Plos One, 2015, 10(10):1-15.
[7]LIU M, ZHONG H, MA E, et al. Resistance to fungal decay of paraffin wax emulsion/copper azole compound system treated wood[J]. International Biodeterioration & Biodegradation, 2018,129:61-66.
[8]王宝峰, 张裕丁, 孙德军. 乳化石蜡的研制及应用[J]. 山东化工, 2004(2):14-17.
WANG Baofeng, ZHANG Yuding, SUN Dejun. Development and application of emulsified paraffin [J]. Shandong Chemical Industry, 2004 (2): 14-17.
[9]KAPUSTIN V M, MAKHIN D Y. Effect of oil content in paraffin on waterproofing properties of paraffin emulsions[J]. Chemistry and Technology of Fuels and Oils, 2012, 48(1):62-66.
[10]罗钰. 纳米的空间限制对表面活性剂吸附和自聚的影响[D].北京:北京化工大学, 2010.
LUO Yu. The influence of nano space limitation on the adsorption and self polymerization of surfactants [D]. Beijing: Beijing University of Chemical Technology, 2010.
[11]罗宏宇. 新型无机/聚合物复合微纳米吸附剂的制备及其对污染物的吸附行为和机理研究[D].镇江:江苏大学, 2015.
LUO Hongyu. Preparation of new inorganic / polymer composite micro nano adsorbent and its adsorption behavior and mechanism for pollutants [D].Zhenjiang: Jiangsu University, 2015.
[12]黄平平. 基于丙烯酸改性液体石蜡制备环保型防水纤维板的研究[D].哈尔滨:东北林业大学2015.
HUANG Pingping. Study on preparation of environmentally friendly waterproof fiberboard based on acrylic modified liquid paraffin [D].Harbin: Northeast Forestry University, 2015.
[13]李光明, 李霞, 贾磊, 等. 国内外磷石膏处理和处置概况[J]. 无机盐工业, 2012, 44(10):11-13.
LI Guangming, LI Xia, JIA Lei, et al. Overview of phosphogypsum treatment and disposal at home and abroad [J]. Inorganic Salt Industry, 2012, 44 (10): 11-13.
[14]李建权, 李国忠, 张国辉. 石膏复合防水剂对石膏晶体形成的影响[J]. 建筑材料学报, 2007, 10(2):137-141.
LI Jianquan, LI Guozhong, ZHANG Guohui. Effect of gypsum composite waterproof agent on gypsum crystal formation [J]. Journal of Building Materials, 2007, 10 (2): 137-141.
[15]潘红, 李国忠. 含氟硅乳液防水剂制备及其对石膏性能的影响[J]. 建筑材料学报, 2013(2):226-231.
PAN Hong, LI Guozhong. Preparation of fluorosilicone emulsion waterproofing agent and its effect on gypsum properties [J]. Journal of Building Materials, 2013 (2): 226-231.
[16]潘红. 含氟硅丙烯酸酯乳液防水剂制备及其在石膏建材中的应用[D].济南:济南大学, 2014.
PAN Hong. Preparation of fluorosilicone acrylate emulsion waterproofing agent and its application in gypsum building materials [D]. Jinan: University of Jinan, 2014.

备注/Memo

备注/Memo:
收稿日期:2019-03-22修改稿日期:2019-11-14
基金项目:国家自然科学基金项目(51662022);昆明理工大学分析测试基金项目(2018M20172210090)
第一作者:赵志曼(1965-),女,博士,教授.主要从事新型材研究.E*mail:lzd 2005@126.com
通信作者:王思骅(1994-),女,硕士生.主要从事新型材料研究.E-mail:964846657@qq.com
更新日期/Last Update: 2020-01-20