[1]王艳,牛荻涛,苗元耀,等.弯曲荷载作用下钢纤维混凝土碳化性能[J].西安建筑科技大学学报:自然科学版,2015,47(01):51-55.[doi:10.15986/j.1006-7930.2015.01.010]
 WANG Yan,NIU Ditao,MIAO Yuanyao,et al.Carbonation of steel fiber reinforced concrete under flexural loading[J].J.Xi’an Univ. of Arch. & Tech.:Natural Science Edition,2015,47(01):51-55.[doi:10.15986/j.1006-7930.2015.01.010]
点击复制

弯曲荷载作用下钢纤维混凝土碳化性能()
分享到:

西安建筑科技大学学报:自然科学版[ISSN:1006-7930/CN:61-1295/TU]

卷:
47
期数:
2015年01期
页码:
51-55
栏目:
出版日期:
2015-02-28

文章信息/Info

Title:
Carbonation of steel fiber reinforced concrete under flexural loading
文章编号:
1006-7930(2015)01-0051-05
作者:
王艳;牛荻涛;苗元耀;关虓;
西安建筑科技大学材料与矿资学院;西安建筑科技大学土木工程学院;
Author(s):
WANG Yan 1 NIU Ditao 2 MIAO Yuanyao2GUAN Xiao2
1 School of Material & Mineral Resources, Xi’an Univ. of Arch. & Tech., Xi’an 710055,China 2 School of Civil Engineering , Xi’an Univ. of Arch. & Tech., Xi’an 710055,China
关键词:
钢纤维混凝土弯曲荷载碳化碳化弯曲应力影响系数
Keywords:
steel fiber reinforced concrete flexural loading carbonization flexural loading influence coefficient on carbonization
分类号:
TU398
DOI:
10.15986/j.1006-7930.2015.01.010
文献标志码:
A
摘要:
实际情况中荷载会对混凝土的耐久性退化规律产生影响,通过开展弯曲荷载作用下钢纤维混凝土的快速碳化试验,研究钢纤维掺量以及应力状态、应力水平对钢纤维混凝土碳化深度的影响规律.结果显示:弯曲荷载对钢纤维混凝土的碳化深度产生了影响,钢纤维混凝土的碳化深度在弯曲拉应力作用下增大,并且随着拉应力水平的提高持续增大;一定水平的弯曲压应力对于钢纤维混凝土的碳化起到抑制作用.适量的钢纤维能够降低弯曲荷载对基体混凝土碳化深度的影响,但当纤维掺量较大时,这种降低效果不再明显.本次试验中,体积掺量为1.5%的钢纤维混凝土在各种应力状态下的碳化深度均为最小,并且受荷载水平的影响也最小.
Abstract:
Loading can affect the degradation rule of concrete durability. Based on the accelerated carbonization test of steel fiber reinforced concrete under flexural loading, effects of steel fiber content, stress state on steel fiber reinforced concrete carbonation depth were studied. Test results indicated that the flexural tensile stress accelerate the concrete carbonation speed, while the flexural compressive stress under a certain level retard the concrete carbonation speed. Right amount of steel fiber helps reduce the influence
of flexural loading on matrix concrete carbonation depth, but the reducing effect was not obvious. According to the varied mixing proportions in the test, steel fiber reinforced concrete of 1.5% volume content producted the best effect, and minimum carbonation depth in varied stress flexural loading.

参考文献/References:

[1] SUN W, ZHANG Y M, YAN H D. et al. Damage and damage resistance of high strength concrete under the action of load and freeze-thaw cycles. Cement and Conerete Researeh, 1999,29(9): 1519-1523.
[2] ZHOU Y, COHEN M D, DOLCH W L. Effect of external loads on the frost-resistant properties of mortar with and without silica fume [J]. ACI Mater J, 1994, 91(6):595-601.
[3] SUN Wei, MU Ru, et al. Effect of chloride salt, freeze–thaw cycling and externally applied load on the performance of the concrete[J]. Cement and Concrete Researech, 2002, 32 (12): 1859-1864.
[4] 余红发, 慕儒, 孙伟, 等.弯曲荷载、化学腐蚀和碳化作用及复合对混凝土抗冻性的影响[J]. 硅酸盐学报,2005,33(4): 492-495.
YU Hongfa, MU Ru, SUN Wei, et al. Effects of flexural loads, chemical attack, carbonation and their combination on Freezing-Thawing durability of concretes [J]. Journal of the Chinese Ceramic Society, 2005, 33(4): 492-495.
[5] 余红发, 孙伟, 李美丹. 荷载对混凝土在腐蚀—冻融作用下强度的影响[J]. 哈尔滨工业大学学报, 2010, 42(2):297-301.
YU Hongfa, SUN Wei, LI Meidan. Effect of flexural stress on strength development of concrete subjected to combined actions of Freezing-Thawing and chemical attack [J]. Journal of Harbin Institute of Technology, 2010,42(2): 297-301.
[6] 孙伟, 余红发, 王晴, 等. 弯曲荷载对混凝土抗卤水冻蚀性的影响[J]. 武汉理工大学学报, 2005, 27(7): 46-49.
SUN Wei, YU Hongfa, WANG Qing, et al. Effect of flexural stress on bittern Freezing-Thawing durability of concrete exposed to salt lakes [J]. Journal of Wuhan University of Technology, 2005, 27(7): 46-49.
[7] 燕坤, 余红发, 麻海燕, 等. 硫酸镁腐蚀与弯曲荷载对碳化混凝土抗冻性的影响[J]. 硅酸盐学报, 2008, 36(7):877-883.
YAN Kun, YU Hongfa, MA Haiyan, et al. Effect of magnesium sulfate attack and flexural stress on Freezing-Thawing durability of carbonized concretes [J].Journal of the Chinese Ceramic Society, 2008, 36(7):877-883.
[8] 何世钦, 贡金鑫. 弯曲荷载作用对混凝土中氯离子扩散的影响[J]. 建筑材料学报, 2005, 8(2): 134-138.
HE Shiqin, GONG Jinxin. Influence of flexural loading on permeability of chloride ion in concrete [J]. Journal of Building Materials, 2005, 8(2): 134-138.
[9] 金祖权, 孙伟, 张云升, 等. 荷载作用下混凝土的碳化深度[J]. 建筑材料学报, 2005, 8(2): 179-183.
JIN Zuquan, SUN Wei, ZHANG Yunsheng, et al. Study on carbonation of concrete under loading [J]. Journal of Building Materials, 2005, 8(2): 179-183.
[10] 张云升, 孙伟, 陈树东, 等. 弯拉应力作用下粉煤灰混凝土的1D 和2D 碳化[J]. 东南大学学报, 2007, 37(1):118-122.
ZHANG Yunsheng, SUN Wei, CHEN Shudong, et al. 1D and 2D carbonation of fly ash concrete under flexural stress [J]. Journal of Southeast University: Natural Science Edition, 2007, 37(1): 118-122.
[11] 郭艳华, 潘慧敏, 李志业. 钢纤维混凝土碳化性能的研究[J]. 混凝土. 2007(2): 45-47.
GUO Yanhua, PAN Huimin, LI Zhiye, Study on carbonation of steel-fiber reinforced concrete[J].Concrete,2007(2): 45-47.
[12] 朱海堂, 高丹盈, 张启明,等. 碳化环境下钢纤维混凝土基本性能试验研究[J]. 郑州大学学报, 2005, 26(3):5-8.
ZHU Haitang, GAO Danying, ZHANG Qiming, et al.Test research on basic properties of steel fiber reinforced concrete under carbonization[J].Journal of Zhengzhou University: Engineering Science, 2005, 26(3): 5-8.
[13] 高丹盈,朱海棠,赵军,等.冻融后钢纤维混凝土力学性能的试验研究[J].郑州大学学报:工学版, 2005, 26(1): 1-4.
GAO Danying, ZHU Haitang, ZHAO Jun, et al. The experimental study on the basic mechanical property of steel fiber reinforced concrete after freeze-thaw [J].Journal of Zhengzhou University: Engineering Science,2005, 26(1): 1-4.
[14] MANGAT P.S, GURUSAMY K. Long Term Properties under Marine Exposure of Steel Fibre Reinforced Concrete Containing PFA [J]. Materials and Structures, 1998, 21(5): 352-358.

相似文献/References:

[1]戴 俊,吴 涛,曹 东,等.微波照射后钢纤维混凝土强度劣化研究[J].西安建筑科技大学学报:自然科学版,2014,46(01):6.[doi:10.15986/j.1006-7930.2014.01.002]
 DAI Jun,WU Tao,CAO Dong,et al.Study on the strength weakening rule of steel fiber reinforced concrete after microwave irradiation[J].J.Xi’an Univ. of Arch. & Tech.:Natural Science Edition,2014,46(01):6.[doi:10.15986/j.1006-7930.2014.01.002]
[2]董必钦,李达谦,张成杰,等.基于变形能的钢纤维混凝土断裂行为量化分析[J].西安建筑科技大学学报:自然科学版,2023,55(04):475.[doi:10.15986/j.1006-7930.2023.04.001 ]
 DONG Biqin,LI Daqian,ZHANG Chengjie,et al.Quantitative analysis of fracture behaviour of steel fibre concrete based on deformation energy[J].J.Xi’an Univ. of Arch. & Tech.:Natural Science Edition,2023,55(01):475.[doi:10.15986/j.1006-7930.2023.04.001 ]

备注/Memo

备注/Memo:
收稿日期:2014-05-10 修改稿日期:2015-02-02
基金项目:国家自然科学基金青年科学基金项目(51308445);陕西省自然科学基金青年人才项目(2013JQ7033);陕西省教育厅专项科研计划项目(2013JK0972)
作者简介:王艳(1982-),女,博士,讲师,主要从事纤维混凝土耐久性方向的研究.E-mail: wangyanwjx@126.com
更新日期/Last Update: 1900-01-01