[1]吴耀鹏,李晓蕾,姜厚文,等.不同配合比再生混凝土高温后的残余抗压强度[J].西安建筑科技大学学报(自然科学版),2017,49(03):375-381.[doi:10.15986/j.1006-7930.2017.03.010]
 WU Yaopeng,LI Xiaolei,JIANG Houwen,et al.Residual compressive strength of recycled aggregate concrete with the different mixture ratio after high temperature[J].J. Xi’an Univ. of Arch. & Tech.(Natural Science Edition),2017,49(03):375-381.[doi:10.15986/j.1006-7930.2017.03.010]
点击复制

不同配合比再生混凝土高温后的残余抗压强度()
分享到:

西安建筑科技大学学报(自然科学版)[ISSN:1006-7930/CN:61-1295/TU]

卷:
49
期数:
2017年03期
页码:
375-381
栏目:
出版日期:
2017-06-30

文章信息/Info

Title:
Residual compressive strength of recycled aggregate concrete with the different mixture ratio after high temperature
文章编号:
1006-7930(2017)03-0375-07
作者:
吴耀鹏1李晓蕾1姜厚文2张冲1
(1.西安建筑科技大学土木工程学院,陕西 西安 710055;2.山西晋投玄武岩开发有限公司,山西 大同037000)
Author(s):
WU Yaopeng1 LI Xiaolei1 JIANG Houwen2 ZHANG Chong1
(1. School of Civil Engineering, Xi′an Univ of Arch & Tech, Xi′an 710055, China; 2. Shanxi Ecic Basalt DevelopmentCo,LTD, Datong 037000, China)
关键词:
高温再生混凝土水胶比粉煤灰
Keywords:
high temperature recycled aggregate concrete water-binder ratio fly-ash
分类号:
TU502.6
DOI:
10.15986/j.1006-7930.2017.03.010
文献标志码:
A
摘要:
浇筑15种配合比的100 mm×100 mm×100 mm混凝土立方体试件,将不同水胶比(0.34、0.4和0.5)、不同粉煤灰掺量(0%、30%和50%)的普通混凝土和再生混凝土试件经200~800 ℃高温处理后进行静压试验,并测得其抗压强度. 结果表明:经400 ℃高温作用后,不同于普通混凝土,水胶比为0.34时的再生混凝土强度低于水胶比为0.4时的强度;对于不同配合比混凝土试件,高温时的强度损失率,低水胶比时较高水胶比时大;粉煤灰的微集料效应可以弥补低水胶比下水泥浆与再生骨料结合面不良的缺陷;粉煤灰的二次水化作用可以有效弥补再生混凝土因高温作用引起的强度损失.
Abstract:
The concrete cube specimens (100 mm×100 mm×100 mm) with 15 kinds of mixture ratios were cast. And the compressive strengths of ordinary and recycled aggregate concrete with different water-binder ratios (0.34, 0.4, and 0.5) and fly-ash dosage (0%, 30%, and 50%) were tested after exposure to high temperature (200~800 ℃). The results show that after exposure to 400 ℃, the compressive strength of recycled aggregate concrete at low water-binder ratio (0.34) is lower than at high water-binder ratio (0.4), which is different from the ordinary concrete. In addition, the compressive strength loss rate of the specimens with lower water-binder ratio is larger than the higher one. The micro-aggregate effect of fly-ash can remedy the poor surface combination between cement and recycled aggregates, especially at low water-binder ratio. And the secondary hydration of fly-ash can compensate for the strength loss of recycled aggregate concrete because of high temperature.

参考文献/References:

[1]肖建庄. 再生混凝土[M]. 北京: 中国建筑工业出版社, 2008. XIAO Jianzhuang. Recycled concrete [M]. Beijing: China Architecture & Building Press, 2008. [2]白国良, 张锋剑, 安昱峄, 等. 再生混凝土承重砌块试验研究[J]. 西安建筑科技大学学报(自然科学版), 2011, 43(1): 7-12. BAI Guoliang, ZHANG Fengjian, AN Yuyi, et al. The research of recycled bearing concrete hollow blocks [J]. J. of Xi′an Univ. of Arch. & Tech., (Natural Science Edition), 2011, 43(1): 7-12. [3]薛建阳, 戚亮杰, 罗峥, 等. 型钢再生混凝土框架—填充墙结构抗震性态水平和容许变形值研究[J]. 西安建筑科技大学学报(自然科学版), 2015, 47(1): 15-20. XUE Jianyang, QI Liangjie, LUO Zheng, et al. Study on seismic performance levels and allowable de-formation values of steel reinforced recycled concrete frame structure with infilled wall [J]. J. of Xi′an Univ. of Arch. & Tech., (Natural Science Edition), 2015, 47(1): 15-20. [4]孔德玉. 天然与再生骨料混凝土水灰比统一定则(Ⅰ)—粗骨料强度的影响[J]. 建筑材料学报, 2003, 6(2): 129-134. KONG Deyu. Unified bolomey′s formula of concrete made with natural and recycled coarse aggregate(Ⅰ)—effect of strength of coarse aggregate[J]. Journal of Building Material, 2003, 6(2): 129-134. [5]肖建庄, 李佳彬, 孙振平,等. 再生混凝土的抗压强度研究[J]. 同济大学学报(自然科学版), 2004, 32(12): 1558-1561. XIAO Jianzhuang, LI Jiabin, SUN Zhenping, et al. Study on compressive strength of recycled aggregate concrete[J]. Journal of Tongji University(Natural Science), 2004, 32(12): 1558-1561. [6]KUTALMLS Recep Akca, OGUR Cakir, et al. Properties of polypropylene fiber reinforced concrete using recycled aggregates [J]. Construction and Building Materials, 2015, 98: 620-630. [7]KOU S C, POON C S. Longterm mechanical and durability properties of recycled aggregate concrete prepared with the incorporation of fly ash [J]. Cement and Concrete Composites, 2013, 37: 12-19. [8]陈爱玖, 王静, 杨粉 纤维再生混凝土力学性能试验及破坏分析[J]. 建筑材料学报, 2013, 2: 244-248. CHEN Aijiu, WANG Jing, YANG Fen. Mechanical properties experiments and failure analysis of fiber recycled concrete[J]. Journal of Building Material, 2013, 2: 244-248. [9]石建光, 许岳周. 骨料级配对再生混凝土强度和工作性能影响的试验研究和计算分析[J]. 混凝土, 2008, 1: 82-86. SHI Jianguang, XU Yuezhou. Experiment research and analysis of aggregate gradation on the strength and workability of recycled concrete[J]. Concrete, 2008, 1: 82-86. [10]ETXEBERRIA M, VAZQUEZ E, MARI A. Influence of amount of recycled coarse aggregates and production process on properties of recycled aggregate concrete [J]. Cement and Concrete Research, 2007, 37: 735-742. [11]PEDRO D, BRITO J, EVANGELISTA L. Influence of the use of recycled concrete aggregates from different sources on structural concrete [J]. Construction and Building Materials, 2014, 71: 141-151. [12]DUAN Z H, POON C S. Properties of recycled aggregate concrete made with recycled aggregates with different amounts of old adhered mortars [J]. Materials and Design, 2014, 58: 19-29. [13]肖建庄, 刘琼, 李文贵. 再生混凝土细微观结构和破坏机理研究[J]. 青岛理工大学学报, 2009, 30(4): 24-30. XIAO Jianzhuang, LIU Qiong, LI Wengui, et al. On the micro- and meso-structure and failure mechanism of recycled concrete[J]. Journal of Qingdao Technological University, 2009, 30(4): 24-30. [14]邓旭华. 水灰比对再生混凝土强度影响的试验研究[J]. 混凝土, 2005, 2: 46-48. DENG Xuhua. Study on effect of compressive strength of recycled aggregate concrete with water cement ratio[J]. Concrete, 2005, 2: 46-48. [15]肖江帆, 史才军, 王德辉, 等. 新拌混凝土水灰比测定方法[J]. 硅酸盐学报, 2012, 11: 1576-1585. XIAO Jiangfan, SHI Caijun, WANG Dehui, et al. Testing methods for determination of water to cement ratio of fresh concrete a short review[J]. Journal of The Chinese Ceramic Society, 2012, 11: 1576-1585. [16]陈文耀, 李文伟. 三峡工程高性能大坝混凝土配合比设计技术措施[J]. 水利学报, 2000, 5: 49-53. CHEN Wenyao, LI Wenwei. The technical measures for the mix design of the concretedam in Three Gorges Project [J]. Journal of Hydraulic Engineering, 2000, 5: 49-53. [17]JOSHI R C, LOHTIA R P, SALAM M A. Some durability related properties of concretes incorporating high volumes of sub-bituminous coal fly ash [C]//3rd CANMET/ACI International Conference on Durability of Concrete, 1994: 447-464. [18]苏益声, 孟二从, 陈宗平, 等. 高温后再生混凝土三轴受压本构关系[J]. 建筑材料学报, 2015, 18(6): 946-952. SU Yisheng, MENG Ercong, CHEN Zongping, et al. Constitutive relations of recycled concrete under triaxial compression after high temperature [J]. Journal of Building Materials, 2015, 18(6): 946-952. [19]徐明, 王韬, 陈忠范. 高温后再生混凝土单轴受压应力—应变关系试验研究[J]. 建筑结构学报, 2015, 36(2): 158-164. XU Ming, WANG Tao, CHEN Zhongfan. Experimental research on uniaxial compressive stress-strain relationship of recycled concrete after high temperature [J]. Journal of Building Structures, 2015, 36(2): 158-164. [20]冯超, 杨海峰, 宁纪源, 等. 高温后再生混凝土受压强度退化及微观结构性能分析[J]. 混凝土, 2016, 4: 24-27. FENG Chao, YANG Haifeng, NING Jiyuan, et al. Compressive strength degradation and micro-structure characteristics of recycled concrete after high temperature [J]. Concrete, 2016, 4: 24-27. [21]万夫雄, 赵鹏辉, 连会杰, 等. 高温后再生混凝土强度与微观机理[J]. 混凝土, 2017, 1: 52-55. WAN Fuxiong, ZHAO Penghui, LIAN Huijie, et al. Strength of recycled concrete after high temperature and its microstructure mechanism [J]. Concrete, 2017, 1: 52-55. [22]张冲. 高温后再生混凝土的残余抗压强度及抗冻耐久性试验研究[D]. 西安: 西安建筑科技大学, 2016. ZHANG Chong. Experimental research on residual compressive strength and freeze-thaw durability of recycled aggregate concrete after high temperatures [D]. Xi′an: Xi′an Univ. of Arch. & Tech., 2016. [23]贾福萍, 王永春, 渠艳艳, 等. 冷却方式和静置时间对高温后混凝土残余强度影响[J]. 建筑材料学报, 2011, 14(3): 400-405. JIA Fuping, WANG Yongchun, QU Yanyan, et al. Influences of various cooling methods and standing time on residual strength of concrete after elevated temperature exposure[J]. Journal of Building Material, 2011, 14(3): 400-405. [24]HWANG K, NOGUCHI T, TOMOSAWA F. Prediction model of compressive strength development of fly-ash concrete [J]. Cement and Concrete Research, 2004, 34(12): 2269-2276.

相似文献/References:

[1]侯 炜,贺拴海,张 岗.防火涂层对高温后混凝土抗压强度的影响[J].西安建筑科技大学学报(自然科学版),2014,46(02):241.[doi:10.15986/j.1006-7930.2004.02.015]
 HOU Wei,HE Shuanhai,ZHANG Gang.Effects of fire protection layer on compressive strength of concreteafter high temperature[J].J. Xi’an Univ. of Arch. & Tech.(Natural Science Edition),2014,46(03):241.[doi:10.15986/j.1006-7930.2004.02.015]
[2]孙传智,王可卿,乔燕,等.高温下600 MPa级高强钢筋力学性能试验研究[J].西安建筑科技大学学报(自然科学版),2019,51(03):355.[doi:10.15986/j.1006-7930.2019.03.008]
 SUN Chuanzhi,WANG Keqing,QIAO Yan,et al.Experimental study on material properties of 600 MPa grade high strength rebar steel at high temperature[J].J. Xi’an Univ. of Arch. & Tech.(Natural Science Edition),2019,51(03):355.[doi:10.15986/j.1006-7930.2019.03.008]
[3]徐金俊,乌忱昊,王 浩,等.再生混凝土绿色建筑碳排放评价及灰色参数敏感性分析[J].西安建筑科技大学学报(自然科学版),2020,52(03):396.[doi:10.15986/j.1006-7930.2020.03.013]
 XU Jinjun,WU Chenhao,WANG Hao,et al.Life cycle assessmentand grey parametric sensitivity analysis on the carbon emission of green building made of recycled aggregate concrete[J].J. Xi’an Univ. of Arch. & Tech.(Natural Science Edition),2020,52(03):396.[doi:10.15986/j.1006-7930.2020.03.013]
[4]姚泽良,崔婷婷,段东旭,等.基于Python的再生混凝土细观性能模拟方法研究[J].西安建筑科技大学学报(自然科学版),2021,53(02):167.[doi:10.15986/j.1006-7930.2021.02.003]
 YAO Zeliang,CUI Tingting,DUAN Dongxu,et al.Research on thesimulation method of mesoscopic performances of recycled concrete based on Python[J].J. Xi’an Univ. of Arch. & Tech.(Natural Science Edition),2021,53(03):167.[doi:10.15986/j.1006-7930.2021.02.003]
[5]李蕾蕾,康 抗,冯泽平,等.冻融与硫酸盐作用下再生混凝土性能劣化研究[J].西安建筑科技大学学报(自然科学版),2023,55(04):571.[doi:10.15986/j.1006-7930.2023.04.012 ]
 LI Leilei,KANG Kang,FENG Zeping,et al.Study on performance deterioration of recycled concrete under coupling effect of freeze-thaw and sulfate[J].J. Xi’an Univ. of Arch. & Tech.(Natural Science Edition),2023,55(03):571.[doi:10.15986/j.1006-7930.2023.04.012 ]

备注/Memo

备注/Memo:
收稿日期:2016-06-25 修改稿日期:2017-05-24 基金项目:国家自然科学基金资助项目(51108371); 陕西省自然科学基础研究基金资助项目(2015JM5164); 西安市工业应用技术研发基金资助项目(CXY1432(4)); 陕西省教育厅重点实验室科研计划基金资助项目(16JS050) 作者简介:吴耀鹏(1979-),男,博士,副教授,主要从事结构抗火研究.E-mail: wyp@ xauat.edu.cn
更新日期/Last Update: 2017-08-27