[1]孙 涛,熊传胜,金祖权,等.焙烧温度对阻锈剂插层水滑石效果的影响[J].西安建筑科技大学学报(自然科学版),2023,55(04):555-562.[doi:10.15986/j.1006-7930.2023.04.010 ]
　SUN Tao,XIONG Chuansheng,JIN Zuquan,et al.Effect of calcination temperature on intercalation hydrotalcite with rust inhibitors[J].J. Xi'an Univ. of Arch. & Tech.(Natural Science Edition),2023,55(04):555-562.[doi:10.15986/j.1006-7930.2023.04.010 ]
点击复制

焙烧温度对阻锈剂插层水滑石效果的影响()
分享到：

西安建筑科技大学学报（自然科学版）[ISSN:1006-7930/CN:61-1295/TU]

卷:
55
期数:
2023年04期
页码:
555-562
栏目:
出版日期:
2023-10-26

文章信息/Info

Title:
Effect of calcination temperature on intercalation hydrotalcite with rust inhibitors
文章编号:
1006-7930(2023)04-0555-08
作者:
孙 涛1; 熊传胜1; 2; 金祖权1; 2; 郭向柯1; 陈兆毅3
(1.青岛理工大学 土木工程学院，山东 青岛 266520; 2.海洋环境混凝土技术教育部工程研究中心，山东 青岛 266520; 3.中国铁路设计集团有限公司，天津 266033)
Author(s):
SUN Tao1;  XIONG Chuansheng1; 2;  JIN Zuquan1; 2;  GUO Xiangke1;  CHEN Zhaoyi3
(1.School of Civil Engineering,Qingdao University of Technology, Qingdao 266033, China; 2.Engineering Research Center of Concrete Technology under Marine Environment, Ministry of Education, Qingdao 266520, China; 3.China Railway Design Corporation, Tianjin 300300, China)
关键词:
镁铝水滑石;  亚硝酸盐;  VB3;  负载率;  形貌变化
Keywords:
layered double hydroxide;  nitrite;  VB3;  loading rate;  change of morphology
分类号:
TU528
DOI:
10.15986/j.1006-7930.2023.04.010
文献标志码:
A
摘要:
研究焙烧温度对NO-2和维生素B3(VB3)两种阻锈剂插层水滑石的影响,通过有机元素和紫外-可见分光光度分析阻锈剂的插层负载率,采用OPC、EIS测试,分析了阻锈剂插层水滑石对钢筋的防护性能,利用SEM和XRD分析插层机理,结论如下:焙烧温度对阻锈剂负载率的影响呈先增后减的趋势.对于NO-2,最佳温度为500 ℃,N元素含量为1.63%,对于VB3,最佳温度为450 ℃,负载率为21.3 wt.%.温度过低,水滑石表面能未被充分激发,温度过高,水滑石层状结构被破坏,阻锈剂难以插层.此外,插层阻锈剂后,水滑石层间距有不同程度的增大,且相比NO-2,插层VB3的水滑石分散更加均匀.
Abstract:
In this paper, the effects of calcined temperature on intercalation hydrotalcite with NO-2 and Vitamin B3(VB3)as rust inhibitors are studied. The intercalation loading rate of rust inhibitor is analyzed by organic elements and UV visible spectrophotometry, the protective performance of the rust inhibitor intercalated hydrotalcite on the steel bar is analyzed by OPC and EIS tests, and the intercalation mechanism is analyzed by SEM and XRD. The conclusion is as follows: the effect of roasting temperature on the loading rate of rust inhibitor increases first and then decreases. For NO-2, the optimum temperature is 500 ℃, and the content of N element is 1.63%. For VB3, the optimum temperature is 450 ℃, and the loading rate is 21.3 wt.%. When the temperature is too low, the surface energy of hydrotalcite is not fully excited, and when the temperature is too high, the layered structure of hydrotalcite is destroyed, and the rust inhibitor is difficult to intercalate. In addition, the interlayer spacing of hydrotalcite increases in different degrees after intercalation of rust inhibitor, and the hydrotalcite intercalated with VB3 is more evenly dispersed than that of NO-2.

参考文献/References:

[1]柯伟.中国工业与自然环境腐蚀调查的进展.腐蚀与防护[J].2004(1):1-8.
KE Wei. Progress in public inquiry concerning corrosion in Chinese industrial and natural environments.Corrosion and protection[J]. 2004(1); 1-8.
[2]HOU B, LI X, MA X, et al. The cost of corrosion in China[J]. NPJ Materials Degradation, 2017, 1(1): 4.
[3]CAO Y, DONG S, ZHENG D, et al. Multifunctional inhibition based on layered double hydroxides to comprehensively control corrosion of carbon steel in concrete[J]. Corrosion Science, 2017, 126: 166-179.
[4]XU J X, SONG Y B. Chloride removal and corrosion inhibitions of nitrate, nitrite-intercalated Mg-Al layered double hydroxides on steel in saturated calcium hydroxide solution[J]. Applied Clay Science, 2018, 163: 129-136.
[5]CAO Y, ZHENG D, DONG S, et al. A composite corrosion inhibitor of Mg-Al layereddouble hydroxides co-intercalated with hydroxide and organic anions for carbon steel in simulated carbonated concrete pore solutions[J]. Cement & Concrete Research, 1981, 11: 383-392.
[6]YANG Z, FISCHER H, CEREZO J, et al. Aminobenzoate modified MgAl hydrotalcites as a novel smart additive of reinforced concrete for anticorrosion applications[J]. Construction & Building Materials, 2013, 47: 1436-1443.
[7]XU J, SONG Y, TAN Q, et al. Chloride absorption by nitrate, nitrite and aminobenzoate intercalated layered double hydroxides[J]. Journal of Materials Science, 2017, 52(10): 5908-5916.
[8]BERNARDO M P, MOREIRA F K V. Synthesis and characterization of eco-friendly Ca-Al-LDH loaded with phosphate for agricultural applications[J]. Applied Clay Science, 2017, 137: 143-150.
[9]吴波.阻锈阴离子插层改性水滑石的制备及其在水泥砂浆中的应用[D]. 深圳:圳大学,2019.
WU Bo. reparation of inhibitor ions intercalation modified hydrotalcite and its application in cement mortar[D]. Shenzhen:Shenzhen University,2019.
[10]CAVANI F, Trifirò F, VACCARI A. Hydrotalcite-type anionic clays: Preparation, properties andapplications[J]. Catalysis Today,1991,11(2):173-301.
[11]赵宇,杨玉彬,徐冰.锌铝水滑石材料的合成及其电化学性能[J].大连交通大学学报,2018,39(5): 48-52.
ZHAOYu,YANG Yubin,XU Bing.Fabricaiton and electrochemical properties of Zn Al-LDHs materials[J]. ournal of Dalian Jiaotong University,2018,39(5): 48-52.
[12]上官荣昌.焙烧温度对镁铝水滑石焙烧产物物性影响的研究[J].淮阴师范学院学报(自然科学版),2002(1): 67-69,73.
SHANGGUAN Rongchang. tudy on the effect of calcination temperature on the physical properties of calcined products of MG-Al hydrotalcite[J].Journal of Huaiyin Teachers College(Natural Science Edition),2002(1): 67-69,73.
[13]生秋平.焙烧水滑石在氯离子环境下对钢筋腐蚀的影响[D].乌鲁木齐:新疆大学,2021.000055.
SHENG Qiuping.Effect of calcined hydrotalcite on steel bar corrosion in chloride Ion Environment[D].Wulumuqi: Xinjiang University,2021.000055.
[14]BRINDLEY G W, KAO C C. Structural and IR relations among brucite-like divalent metal hydroxides[J]. Physics & Chemistry of Minerals, 1984, 10(4): 187-191.
[15]EVANS D G, DUAN X. Preparation of layered double hydroxides and their applications as additives in polymers, as precursors to magnetic materials and in biology and medicine[J]. Chemical Communications, 2006, 37(15): 485-496.
[16]WANG Y, ZHANG D. Synthesis, characterization, and controlled release anticorrosion behavior of benzoate intercalated Zn-Al layered double hydroxides[J]. Materials Research Bulletin, 2012, 47(11): 3185-3194.
[17]CHEN Y, SHUI Z, CHEN W, et al. Chloride binding of synthetic Ca-Al-NO3 LDHs in hardened cement paste[J]. Construction and Building Materials, 2015, 93: 1051-1058.

备注/Memo

备注/Memo:
收稿日期:2022-11-11修回日期:2023-07-15
基金项目:国家自然科学基金项目(51709253); 中国国家铁路集团有限公司重点课题基金资助项目(N2020G055); 宁波市科技创新2025重大专项基金资助项目(2020Z035)
第一作者:孙 涛(1998—)，男，硕士，主要从事海洋环境混凝土结构耐久性研究.E-mail:885351839@qq.com
通信作者:熊传胜(1987—)，男，副教授，硕士生导师，主要从事于水泥基复合材料及其耐久性、材料的腐蚀与防护技术等相关研究工作.E-mail:xiongcs@qut.edu.cn
更新日期/Last Update: 2023-08-28