[1]薛 刚,林大地.橡胶混凝土低温抗折性能试验研究[J].西安建筑科技大学学报(自然科学版),2019,51(05):623-628.[doi:10.15986/j.1006-7930.2019.010.002]
　XUE Gang,LIN Dadi.Experimental study on flexural behavior of rubber concrete at low temperature[J].J. Xi’an Univ. of Arch. & Tech.(Natural Science Edition),2019,51(05):623-628.[doi:10.15986/j.1006-7930.2019.010.002]
点击复制

橡胶混凝土低温抗折性能试验研究()
分享到：

西安建筑科技大学学报（自然科学版）[ISSN:1006-7930/CN:61-1295/TU]

卷:
51
期数:
2019年05期
页码:
623-628
栏目:
出版日期:
2019-12-05

文章信息/Info

Title:
Experimental study on flexural behavior of rubber concrete at low temperature
文章编号:
1006-7930(2019)05-0623-06
作者:
薛 刚;  林大地
(内蒙古科技大学 土木工程学院 内蒙古 包头 014010)
Author(s):
XUE Gang; LIN Dadi
(School of Civil Engineering, Inner Mongolia University of Science and Technology, Inner Mongolia Baotou 014010, China)
关键词:
橡胶混凝土;  低温抗折;  橡胶掺量;  强度提高系数;  折压比
Keywords:
rubber concrete;  low temperature;  water-to-binder ratio;  flexural strength;  bend-press ratio
分类号:
TU411
DOI:
10.15986/j.1006-7930.2019.010.002
文献标志码:
A
摘要:
在水灰比分别为0.35、0.40、0.45中分别以0、10%,20%和30%的橡胶掺量配制橡胶混凝土,分别在-30 ℃、20 ℃环境下进行橡胶混凝土抗折性能研究.结果表明:低温下橡胶混凝土破坏状态和常温下相比基本一致,随着橡胶掺量增大,破坏时试件显示出一定保持整体形态的能力.常温20 ℃时,随着橡胶掺量的增加,橡胶混凝土的抗折强度降低,且下降趋势越来越快.在低温环境下,橡胶混凝土试件的抗折强度提高系数随着橡胶掺量的增加,表现出先下降后上升的趋势.在橡胶掺量相同的情况下,随着橡胶混凝土的水灰比的增加,抗折强度也提高,同时提高系数也增加; 在低温环境下,橡胶混凝土折压比变化情况与常温下的变化情况相似,低温的折压比高于常温情况,表明橡胶混凝土在低温仍具有良好的韧性.
Abstract:
Four kinds of rubber content concrete were prepared in three kinds of water-to-binder ratios of 0.35, 0.40 and 0.45, and the study of the flexural performance test was carried out at low temperature-30 °C and normal temperature at 20 °C. Result shows that the failure feature of the rubber concrete at low temperature is basically the same as that under normal temperature. With the increase of rubber content, the test piece shows the ability to maintain the overall shape. At the temperature of 20 °C, the flexural strength decreases with the increase of the rubber content, and the downward trend is accelerated. At low temperature, as the rubber content increases, the flexural strength increase coefficient appears to decrease first and then increase. When the rubber content is the same, the flexural strength of the rubber concrete increased as the water-to-binder ratio increases, and the coefficient of the flexural strength increases as well. With the increase of rubber content, the change trend of low temperature bend-press ratio of rubber concrete is similar to that of the normal temperature. The bend-press ratio at low temperature is higher than the normal temperature, which indicates that the rubber concrete still has good toughness at low temperatures.

参考文献/References:

[1] 中华人民共和国商务部.中国再生资源回收行业发展报告2017[J]. 资源再生,2017(5):16-25.Ministry of Commerce of P. R. C. China renewable resources recycling industry development report(2017)[J]. Resource Regeneration, 2017(5): 16-25
[2] 梅大鹏. 废旧轮胎在道路工程中的应用[J]. 中国轮胎资源综合利用,2017(8): 31-34.MEI Dapeng. Application of used tires in road engineering[J]. Comprehensive Utilization of China’s tire resources, 2017(8): 31-34.
[3] BISHT K, RAMANA P V. Evaluation of mechanical and durability properties of crumb rubber concrete[J]. Construction and Building Materials,2017,(155):811-817.
[4] 李赞成,许金余. 橡胶混凝土的基本力学特性的试验研究[J]. 硅酸盐通报,2013,32(12):2589-2594.LI Zancheng, XU Jinyu. Experimental study on the basic mechanical properties of rubber powder[J]. Bulletin of the Chinese Ceramic Society, 2103, 32(12): 2589-2594
[5] 杨春峰,杨敏. 废旧橡胶混凝土力学性能研究进展[J]. 混凝土,2011(12):98-100,109.YANG Chunfeng, YANG Min. Research progress on mechanical performance of waste rubber concrete[J]. Concrete, 2011(12): 98-100,109
[6] 陈胜霞,张亚梅. 橡胶颗粒细度、掺量及成型工艺对橡胶混凝土抗冻性能的影响[J]. 工业建筑,2013,43(增刊):617-621.CHEN Shengxia, ZHANG Yamei. Influence of rubber fineness, content and casting method on frost resistance of recycled rubber concrete[J]. Industrial Construction, 2013,43(S): 617-621
[7] 张永明,朱涵,杨林虎. 低温下等强橡胶集料混凝土的脆性初探[J]. 天津大学学报,2009,42(3):190-193.ZHANG Yongming, ZHU Han, YANG Linhu. Brittleness of CRC of equal strengh at low tmperature[J]. Journal of Tianjin University, 2009, 42(3): 190-193.
[8] MONFORE G E, LENTZ A E. Physical properties of concrete at very low temperatures [J]. J. PCA.1962, 4(2):33-39.
[9] 山根昭. 超低温技术[J]. 低温建筑技术,1980,2(1):57-60.SHAN Genzhao. Ultra-low temperature technology[J] Low Temperature Building Technology, 1980, 2(1)57-60.
[10]李响,谢剑,吴洪海. 超低温环境下混凝土本构关系试验研究[J]. 工程力学,2014,31(增刊):195-200.LI Xiang,XIE Jian, WU Honghai. Experimental research on the constitutive relationship of concrete in a cryogenic environment[J]. Engineering Mechanics, 2014, 31(S): 195-200.
[11]王传星,谢剑,李慧杰. 低温环境下混凝土性能试验研究[J]. 工程力学,2011,28(增刊Ⅱ):182-186.WANG Chuangxing, XIE Jian,. LI Huijie. Experimental research on the properties of concrete under low-temperature[J] Engineer Mechanics, 2011, 28(SⅡ): 182-186.
[12]时旭东,居易. 混凝土低温受拉强度试验研究[J]. 建筑结构,2016,46(16):86-89.SHI Xudong, JU Yi. Experimental study on tensile strength of concrete exposed to cryogenic temperature[J]. Building Structure, 2016, 46(16): 86-89.
[13]张楠,廖娟. 混凝土低温力学性能及试验方法[J]. 硅酸盐学报,2014,42(11):1404-1408.ZHANG Nan, LIAO Juan.Testing method and mechanical properties of concrete at low temperature[J]. Journal of the Chinese Ceramic Society, 2014, 42(11): 1404-1408
[14]YANG Linhu, HAN Zhu, LI Chengfang. Strengths and flexural strain of CRC specimens at low temperature [J]. Construction and Building Materials.2011, 25: 906-910.

相似文献/References:

[1]郭 琦,吴 梦,孙虎平,等.考虑初始随机缺陷的橡胶混凝土破坏形态研究[J].西安建筑科技大学学报(自然科学版),2020,52(06):806.[doi:10.15986/j.1006-7930.2020.06.005 ]
　GUO Qi,WU Meng,SUN Huping,et al.Study of rupture form for rubber concrete considering initial random defect[J].J. Xi’an Univ. of Arch. & Tech.(Natural Science Edition),2020,52(05):806.[doi:10.15986/j.1006-7930.2020.06.005 ]

备注/Memo

备注/Memo:
收稿日期:2018-10-18 修改稿日期:2019-09-20基金项目:国家自然科学基金资助项目(51868063)第一作者:薛刚(1968-),男,教授,博士,主要从事结构振动与控制、高性能混凝土的研究、橡胶混凝土的研究xuegang-2008@126.com通讯作者:林大地(1992-),男,硕士研究生,主要从事高性能混凝土、橡胶混凝土的研究CooperLin92@163.com
更新日期/Last Update: 2019-12-05