[1]王柏文,刘 扬,王 龙,等.疲劳荷载下锈蚀钢筋混凝土粘结性能研究[J].西安建筑科技大学学报(自然科学版),2019,51(05):643-648.[doi:10.15986/j.1006-7930.2019.010.005]
　WANG Bowen,LIU Yang,WANG Long,et al.Bond behavior of corroded reinforced concrete under fatigue loading[J].J. Xi’an Univ. of Arch. & Tech.(Natural Science Edition),2019,51(05):643-648.[doi:10.15986/j.1006-7930.2019.010.005]
点击复制

疲劳荷载下锈蚀钢筋混凝土粘结性能研究()
分享到：

西安建筑科技大学学报（自然科学版）[ISSN:1006-7930/CN:61-1295/TU]

卷:
51
期数:
2019年05期
页码:
643-648
栏目:
出版日期:
2019-12-05

文章信息/Info

Title:
Bond behavior of corroded reinforced concrete under fatigue loading
文章编号:
1006-7930(2019)05-0643-06
作者:
王柏文1; 2; 刘 扬1; 2; 王 龙1; 2; 张 明1; 2
(1. 长沙理工大学 土木与建筑学院,湖南 长沙 410114; 2.桥梁工程安全控制省部共建教育部重点实验室,湖南 长沙 410114)
Author(s):
WANG Bowen1; 2; LIU Yang1; 2; WANG Long1; 2; ZHANG Ming1; 2
(1. School of Civil Engineering and Architecture,Changsha University of Science & Technology,Changsha 410114,China;2. Key Laboratory for Safety Control of Bridge Engineering,Ministry of Education and Hunan Province,Changsha 410114,China)
关键词:
复合作用;  钢筋混凝土;  粘结性能;  疲劳:锈蚀
Keywords:
composite action;  reinforced concrete;  bonding properties;  fatigue: corrosion
分类号:
U444
DOI:
10.15986/j.1006-7930.2019.010.005
文献标志码:
A
摘要:
为研究复合作用对混凝土与钢筋间粘结性能的影响,设计制作了一批变形钢筋混凝土粘结试件.在疲劳和加速锈蚀同时进行后,通过粘结试件的拔出试验得到混凝土与钢筋间粘结应力 - 滑移曲线,分析了复合作用对粘结应力 - 滑移曲线影响,并且总结了钢筋混凝土粘结试件破坏模式.试验研究表明:在复合作用下,钢筋混凝土试件的失效模式大致可分为两类:劈裂破坏、剪切破坏.其中低循环疲劳荷载作用下的试件多出现劈裂破坏,而高循环疲劳荷载作用下的试件多为剪切破坏; 在单一因素作用下,试件的粘结应力分布基本呈“单峰”分布,而在复合作用下,应力分布曲线呈“双峰”分布; 复合作用后,极限粘结应力及试件破坏时滑移值都出现了一定程度的降低.
Abstract:
In order to study the effect of composite action on the bonding properties between concrete and reinforcement, a batch of deformed reinforced concrete specimens was designed and manufactured. After fatigue and accelerated corrosion were performed at the same time, the bond stress-slip curve about concrete and steel was obtained through the pull-out test. The effect of composite action on the bond stress-slip curve was analyzed, and the destruction mode was discussed. The research shows that under the composite action, the failure modes of reinforced concrete specimens can be roughly divided into two categories: splitting failure, and shear failure. Among the specimens under low cyclic fatigue loading, there are many cracking failures, while the test specimens under high cyclic fatigue load are mostly shear failures. Under the influence of single factor, the bond stress distribution of the specimens basically shows a “single peak”. The stress distribution curve presents a “double peak” under the combined effect. After the composite action, the ultimate bond stress and the slip value of the test piece were all reduced to some extent.

参考文献/References:

[1] 赵羽习,金伟良.钢筋与混凝土粘结本构关系的试验研究[J]. 建筑结构学报,2002,23(1):32-36.ZHAO Yuxi, JIN Weiliang. Experimental study on the constitutive relationship between steel and concrete[J]. Journal of Building Structures, 2002,23(1):32-36.
[2] PARK R, PAULAY T. Reinforced concrete structures[M]. New York: Wiley&Sons,1975.
[3] 张伟平, 顾祥林, 金贤玉,等.混凝土中钢筋锈蚀机理及锈蚀钢筋力学性能研究[J]. 建筑结构学报, 2010(S1):327-332.ZHANG Weiping, GU Xianglin, JIN Xianyu, et al. Corrosion mechanism of steel in concrete and mechanical properties of corroded steel bars[J].Journal of Building Structures,2010(S1):327-332.
[4] 贡金鑫,王海超,李金波.腐蚀环境中荷载作用对钢筋混凝土梁腐蚀的影响[J].东南大学学报(自然科学版), 2005,35(3):421-426.GONG Jinxing, WANG Haichao, JIN Haibo. Influence of load on corrosion of reinforced concrete beams in corrosive environment[J].Journal of Southeast University(Natural Science Edition), 2005,35(3):421-426
[5] 王海超,贡金鑫,宋元成.钢筋混凝土梁腐蚀疲劳的试验研究[ J].建筑结构学报,2004,25(5):105～110,123.WANG Haichao, GONG Jinxing, SONG Yuancheng. Experimental study on corrosion fatigue of reinforced concrete beams [J]. Journal of Building Structures, 2004,25(5):105～110,123.
[6] 陈静.锈蚀钢筋混凝土构件粘结力的退化及其对承载力的影响[D].上海:上海交通大学,2008.CHEN Jing.Degradation of bond strength of corroded reinforced concrete members and its influence on bearing capacity [D]. Shanghai:Shanghai Jiaotong University,2008
[7] FANG Congqi, Karin Lundgren. Corrosion influence on bond in reinforced concrete[J] Cement and Concrete Research, 2004(34): 2159-2167.
[8] 郑晓燕,吴胜兴. 动荷载下锈蚀钢筋混凝土粘结滑移特性的试验研究[J].土木工程学报,2006,39(6):42-46ZHENG Xiaoyan,WU Shengxing, Experimental study on bond-slip characteristics of corroded reinforced concrete under dynamic loading[J].China Civil Engineering Journal,2006,39(6):42-46.
[9] 王磊,马亚飞. 锈蚀钢筋粘结性能对比试验研究[J].公路交通科技,2010,27(6):91-96.WANG Lei,MA Yafei. Experimental study on bonding performance of corroded steel bars[J]. Highway Traffic Science and Technology,2010,27(6):91-96.
[10]Kapilesh Bhargava, GHOSH A K. Corrosion-induced bond strength degradation in reinforced concrete: analytical and empirical models[J] Nuclear Engineering and Design, 2007(10): 1140-1157.
[11]彭修宁,金志良,薛建阳,等. 疲劳荷载下锈损钢筋混凝土粘结性能退化试验研究[J].工业建筑,2010,40(2):101-104.PENGXiuning, JIN Zhiliang, XUE Jianyang, et al. Experimental study on the bondage degradation of rust-damaged reinforced concrete under fatigue loading[J].Industrial Construction,2010,40(2):101-104.
[12]范进,董福兴. 疲劳荷载下钢筋锈蚀混凝土构件粘结性能试验研究[J].南京理工大学学报,2009,33(6):734-738.FAN Jin, DOGN Fuxing. Experimental study on bond behavior of reinforced concrete members under fatigue loading[J].Journal of Nanjing University of Science and Technology, 2009,33(6):734-738.
[13]洪小健,张誉.粘结滑移试验中的粘结应力的拟合方法[J]. 结构工程师,2000(3):44-48.HONGXiaojian, ZHANG Yu. Fitting method of bond stress in bond-slip test[J]. Structural Engineer, 2000(3):44-48.

相似文献/References:

[1]蔡渝新,刘清风.混凝土拌合物稳定性及其对工程结构耐久性影响的研究进展[J].西安建筑科技大学学报(自然科学版),2023,55(04):492.[doi:10.15986/j.1006-7930.2023.04.003 ]
　CAI Yuxin,LIU Qingfeng.Research progress on the stability of concrete mixtures and its influence on the durability of engineering structures[J].J. Xi’an Univ. of Arch. & Tech.(Natural Science Edition),2023,55(05):492.[doi:10.15986/j.1006-7930.2023.04.003 ]

备注/Memo

备注/Memo:
收稿日期:2018-07-24 修改稿日期:2019-09-20基金项目:国家重点基础研究发展计划基金次目(973计划)(2015CB057705)第一作者:王柏文(1993-),男,博士研究生; 主要从事桥梁可靠度研究.E-mail:wangbowen-bridge@qq.com
更新日期/Last Update: 2019-12-05